GB 175-2007 通用硅酸盐水泥 |
|||
|
Clause |
Test Items |
Test method |
|
|
条款 |
测试项目 |
测试方法 |
|
|
1 |
compressivestrenth Mpa(psi)(3,28days) |
GB/T 17671 |
|
|
强度（3天,28天） |
|||
|
2 |
soundness |
GB/T 750 |
|
|
安定性 |
|||
|
3 |
fineness, |
GB/T 1345 |
|
|
细度 |
|||
|
4 |
time of setting |
GB/T 1346 |
|
|
凝结时间 |
|||
|
5 |
loss on ignition, max, % |
GB/T 176-2008 |
|
|
烧失量 |
|||
|
6 |
insoluble residue,max,% |
GB/T 176-2008 |
|
|
不溶物 |
|||
|
7 |
magnesium oxide(MgO), max,% |
GB/T 176-2008 |
|
|
氧化镁含量 |
|||
|
8 |
sulfur trioxide(SO3), MAX, % |
GB/T 176-2008 |
|
|
三氧化硫含量 |
|||
|
9 |
CaO,% |
GB/T 176-2008 |
|
|
氧化钙含量 |
|||
|
10 |
f-CaO,% |
GB/T 176-2008 |
|
|
游离氧化钙含量 |
|||
|
11 |
aluminum oxide(Al2O3), max, % |
GB/T 176-2008 |
|
|
三氧化二铝含量 |
|||
|
12 |
sillicon dioxide (SiO2), min, % |
GB/T 176-2008 |
|
|
二氧化硅含量 |
|||
|
13 |
ferric oxide (Fe2O3), max, % |
GB/T 176-2008 |
|
|
三氧化二铁含量 |
|||
|
14 |
alkali（K+,Na+） |
GB/T 176-2008 |
|
|
碱含量（钾离子，钠离子） |
|||
|
15 |
Expand (1day/3days/7days/14days) |
JC/T313-1996 |
|
|
膨胀率(1天/3天/7天/14天) |
|||
|
|
|
|
|
|
EN |
|||
|
Clause |
Test Item |
Test Method |
|
|
条款 |
测试项目 |
测试方法 |
|
|
1 |
Compressivestrenth Mpa(psi)(2,7,28days) |
EN 196-1:2005 |
|
|
抗压强度(2,7,28天) |
|||
|
2 |
Soundness |
EN 196-3: 2005 |
|
|
安定性 |
|||
|
3 |
Fineness |
EN 196-6:1992 |
|
|
细度 |
|||
|
4 |
setting time |
EN 196-3: 2005 |
|
|
凝结时间 |
|||
|
5 |
loss on ignition, % |
EN 196-2: 2005 |
|
|
烧失量 |
|||
|
6 |
Insoluble residue, % |
EN 196-2: 2005 |
|
|
不溶物 |
|||
|
7 |
Sulfate content |
EN 196-2: 2005 |
|
|
(as SO3), % |
|||
|
硫酸盐含量（折算SO3含量） |
|||
|
8 |
Chloride content,% |
EN |
|
|
氯离子含量 |
|||
|
ASTM C 150(99a） |
|||
|
Clause |
Test Items |
Test method |
|
|
条款 |
测试项目 |
测试方法 |
|
|
1 |
compressivestrenth |
ASTM C 109/109M |
|
|
Mpa(psi)(1days) |
|||
|
强度（1天） |
|||
|
2 |
compressivestrenth Mpa(psi)(3days) |
ASTM C 109/109M |
|
|
强度（3天） |
|||
|
3 |
compressivestrenth Mpa(psi)(7days) |
ASTM C 109/109M |
|
|
强度（7天） |
|||
|
4 |
compressivestrenth Mpa(psi)(28days) |
ASTM C 109/109M |
|
|
强度（28天） |
|||
|
5 |
Autoclave Expansion |
ASTM C 151 |
|
|
压蒸安定性 |
|||
|
6 |
Density |
ASTM C 188 |
|
|
密度 |
|||
|
7 |
ari content of mortar,% |
ASTM C 185 |
|
|
胶砂含气量，％ |
|||
|
8 |
time of setting |
ASTM C 191 |
|
|
凝结时间 |
|||
|
Normal Consistency |
ASTM C 187 |
||
|
标准稠度用水量 |
|||
|
9 |
sillicon dioxide (SiO2), min, % |
ASTM C 114 |
|
|
二氧化硅含量 |
|||
|
10 |
aluminum oxide(Al2O3), max,% |
ASTM C 114 |
|
|
三氧化二铝含量 |
|||
|
11 |
ferric oxide (Fe2O3), max, % |
ASTM C 114 |
|
|
三氧化二铁含量 |
|||
|
12 |
magnesium oxide(MgO), max,% |
ASTM C 114 |
|
|
氧化镁含量 |
|||
|
13 |
sulfur trioxide(SO3), max, % |
ASTM C 114 |
|
|
三氧化硫含量 |
|||
|
14 |
CaO,% |
ASTM C 114 |
|
|
氧化钙含量 |
|||
|
|
|
||
广东水泥测试有什么标准